Net structure and method of making

ABSTRACT

The present invention concerns an extrusion formed reticulated web, mesh or netting including reticulated hook fasteners for use with hook and loop fasteners the polymer netting comprising two sets of strands at angles to each other. The first set of strands are a plurality of oriented (molecular orientation created by stretching) strands extending in a first direction and are generally mutually parallel and linear. The second set of strands are a plurality of substantially parallel strands attached only to a first face of the first set of oriented strands. The first set of oriented strands occupy a first planar cross-sectional area in the thickness direction of the formed netting. Said second set of oriented strands occupy a second planar cross-sectional area in the thickness direction of the formed netting. Preferably, these first and second planar cross-sectional areas are substantially mutually exclusive and are abutting. The polymer netting is preferably made by extruding a thermoplastic resin through a die plate, which die plate is shaped to form a base film layer and spaced ridges or ribs projecting from a surface of the base layer. The spaced ridges or ribs formed by the die form the first set of strands forming the reticulated mesh or netting. The second set of transverse strands are formed by transversely cutting the base layer at spaced locations along a length, at a transverse angle to the ridges or ribs, to form discrete cut portions. Subsequently longitudinal stretching of the ridges (in the direction of the ridges or the machine direction) separates these cut portions of the backing, which cut portion then form the second set of spaced apart strands of the reticulated mesh or netting.

SUMMARY OF THE INVENTION

The present invention concerns an extrusion formed reticulated web, meshor netting including reticulated hook fasteners for use with hook andloop fasteners.

BACKGROUND OF THE INVENTION

A method of forming a reticulated hook element is disclosed in U.S. Pat.No. 4,001,366 which describes forming hooks by known methods, similar tothat disclosed in U.S. Pat. Nos. 4,894,060 and 4,056,593, discussedbelow. A reticulated web or mesh structure is formed by intermittentlyslitting (skip slit) extruded ribs and bases and then pulling to expandthe skip slit structure into a mesh.

U.S. Pat. No. 5,891,549 describes a method for forming a net sheethaving surface protrusions thereon. The net is used primarily as spacerelements for drainage and like applications. The net has parallelelements that extend at right angles to each other and it would appearto be formed by a direct molding process involving directly extrudingthe net-like structure onto a negative mold of the netting.

A film extrusion process for forming hooks is proposed, for example, inU.S. Pat. Nos. 4,894,060 and 4,056,593, which permits the formation ofhook elements by forming rails on a film backing. Instead of the hookelements being formed as a negative of a cavity on a molding surface, asis the more traditional method, the basic hook cross-section is formedby a profiled film extrusion die. The die simultaneously extrudes thefilm backing and rib structures. The individual hook elements are thenpreferably formed from the ribs by cutting the ribs transversely,followed by stretching the extruded strip in the direction of the ribs.The backing elongates but the cut rib sections remain substantiallyunchanged. This causes the individual cut sections of the ribs toseparate each from the other in the direction of elongation formingdiscrete hook elements. Alternatively, using this same type extrusionprocess, sections of the rib structures can be milled out to formdiscrete hook elements. With this profile extrusion, the basic hookcross section or profile is only limited by the die shape and hooks canbe formed that extend in two directions and have hook head portions thatneed not taper to allow extraction from a molding surface.

BRIEF DESCRIPTION OF THE INVENTION

The present invention is directed at a polymer netting comprising twosets of strands at angles to each other. The first set of strands are aplurality of oriented (molecular orientation created by stretching)strands extending in a first direction and are generally mutuallyparallel and linear. These first set of strands have a first face and asecond face and two side faces. The second set of strands are aplurality of substantially parallel strands attached only to said firstface of the first set of oriented strands. The second set of strandsalso have a first face and a second face and two substantially parallelside faces, where said second set of strands second faces are attachedto said first set of oriented strands. The first set of oriented strandsoccupy a first planar cross-sectional area in the thickness direction ofthe formed netting. Said second set of oriented strands occupy a secondplanar cross-sectional area in the thickness direction of the formednetting. Preferably, these first and second planar cross-sectional areasare substantially mutually exclusive and are abutting. The polymernetting is preferably made by a novel adaptation of a known method ofmaking hook fasteners as described, for example, in U.S. Pat. Nos.3,266,113; 3,557,413; 4,001,366; 4,056,593; 4,189,809 and 4,894,060 oralternatively U.S. Pat. No. 6,209,177, the substance of which areincorporated by reference in their entirety.

The preferred method generally includes extruding a thermoplastic resinthrough a die plate, which die plate is shaped to form a base film layerand spaced ridges or ribs projecting from a surface of the base layer.The spaced ridges or ribs formed by the die form the first set ofstrands forming the reticulated mesh or netting. The second set oftransverse strands are formed by transversely cutting the base layer atspaced locations along a length, at a transverse angle to the ridges orribs, to form discrete cut portions. Subsequently longitudinalstretching of the ridges (in the direction of the ridges or the machinedirection) separates these cut portions of the backing, which cutportion then form the second set of spaced apart strands of thereticulated mesh or netting. The stretching also orients the ridgesincreasing their strength and flexibility.

In a preferred method a die plate is shaped to form a base film layerand spaced ridges, ribs or hook elements projecting from both surfacesof the base layer. The optional second set of ridges generally forms thecross-section shapes of the desired discrete projections to be produced,which are preferably hook members. The initial hook member thickness isformed by transversely cutting these secondary ridges and the base atspaced locations along their lengths to form discrete cut portions ofthe base with the ridges. Subsequently longitudinal stretching of thebacking layer (in the direction of the ridges on the machine direction)separates these discrete cut portions, which cut portions then form thesecond set of spaced apart strands having projections or hook members,that have a cross-sectional shape identical to the cross-sectional shapeof the second set of extruded ridges.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be further described with reference to theaccompanying drawings wherein like reference numerals refer to likeparts in the several views, and wherein:

FIG. 1 schematically illustrates a method for making a netting such asshown in FIGS. 2–4.

FIG. 2 is a perspective view of a precursor film used to make thenetting of FIG. 4.

FIG. 3 is a perspective view of a first embodiment netting cut precursorfilm in accordance with the present invention.

FIG. 4 is a perspective view of a first embodiment netting in accordancewith the present invention.

FIG. 5 is a perspective view of a second embodiment netting inaccordance with the present invention having hook elements.

FIGS. 6 a and 6 b are enlarged fragmentary side and end views,respectively, of one hook member such as those of the mesh hook nettingof FIG. 5.

FIG. 7 is an enlarged fragmentary sectional view of an alternativeembodiment hook portion that can be made according to the presentinvention.

FIG. 8 is an enlarged fragmentary sectional view of an alternativeembodiment hook portion that can be made according to the presentinvention.

FIG. 9 is a perspective view of another netting in accordance with thepresent invention.

FIG. 10 is a perspective view of another netting in accordance with thepresent invention having hook elements.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

A first embodiment method for forming a reticulated mesh or netting,such as that of FIG. 4, is schematically illustrated in FIG. 1.Generally, the method includes first extruding a strip 50 such as thestrip 1, shown in FIG. 2, of thermoplastic resin from an extruder 51through a die 52 having an opening cut, for example, by electrondischarge machining, shaped to form the strip 50 with a base 3, andelongate spaced ribs 2 projecting from at least one surface 5 of thebase layer 3 that have a predetermined cross sectional shape. Ifdesired, a second set of ridges or ribs can be provided on the secondsurface 4 of the base layer 3 which second set of ridges can have anypredetermined shape, including that of a desired hook portions ormembers. The strip 50 is pulled around rollers 55 through a quench tank56 filled with a cooling liquid (e.g., water), after which the baselayer 3 is transversely slit or cut at spaced locations 7 along itslengths by a cutter 58 to form discrete portions 6 of the base layer 3.The distance between the cut lines corresponds to about the desiredwidth 11 of the strand portions 9 to be formed, as is shown in FIG. 4.The cuts 7 can be at any desired angle, generally from 90° to 30° fromthe lengthwise extension of the ribs 2. Optionally, the strip can bestretched prior to cutting to provide further molecular orientation tothe polymers forming the base layer 3 or ribs 2 and reducing the size ofthe ridges or ribs 2 or base layer thickness 12 and also reducing thesize of the strands 9 formed by slitting of the base layer 3. The cutter58 can cut using any conventional means such as reciprocating orrotating blades, lasers, or water jets, however preferably it cuts usingblades oriented at an angle of about 60 to 90 degrees with respect tolengthwise extension of the ribs 2.

After cutting of the base layer 3, the ridges or ribs 2 of the strip 50are longitudinally stretched at a stretch ratio of 1.5, and preferablyat a stretch ratio of at least about 3.0, preferably between a firstpair of nip rollers 60 and 61 and a second pair of nip rollers 62 and 63driven at different surface speeds. This forms the first set of orientedstrands 8. Optionally, the strip 5O can also be transversely stretchedto provide orientation to the strands 9 in their lengthwise extension.The method would apply to all embodiments of the invention. Roller 61 ispreferably heated to beat the base 3 prior to stretching, and the roller62 is preferably chilled to stabilize the stretched base 3. Stretchingcauses spaces 13 between the cut portions 6 of the base layer 3, whichthen become the second set of strands 9 for the completed netting 10.

Formed hook members if present can also be heat treated preferably by anon-contact heat source 64. The temperature and duration of the heatingshould be selected to cause shrinkage or thickness reduction of at leastthe head portion by from 5 to 90 percent. The heating is preferablyaccomplished using a non-contact heating source which can includeradiant, hot air, flame, UV, microwave, ultrasonics or focused IR heatlamps. This heat treating can be over the entire strip containing theformed hook portions or can be over only a portion or zone of the strip.Or different portions of the strip can be heat treated to more or lessdegrees of treatment. In this manner, it is possible to obtain on asingle strip hook containing areas with different levels of performancewithout the need to extrude different shaped rib profiles. This heattreatment can change hook elements continuously or in gradients across aregion of the hook strip. In this manner, the hook elements can differcontinuously across a defined area of the hook member. Further, the hookdensity can be the same in the different regions coupled withsubstantially the same film backing caliper or thickness (e.g., 50 to500 microns). The caliper can easily be made the same as the hook stripwill have the same basis weight and same relative amount of materialforming the hook elements and backing in all regions despite thedifference in the shape of the hooks caused by the subsequent heattreating. The differential heat treatment can be along different rows orcan cut across different rows, so that different types of hooks, such ashooks having different hook thicknesses, can be obtained in a single ormultiple rows in the machine direction or the lengthwise direction ofthe hook strip. The heat treatment can be performed at any timefollowing creation of the hook element, such that customized performancecan be created without the need for modifying the basic hook elementmanufacturing process.

Referring now to FIG. 5, an exemplary polymeric mesh hook fastenerportion, which can be produced, according to the present invention,generally designated by the reference numeral 14 is shown. The mesh hooknetting comprises strands 20 having generally parallel upper and lowermajor surfaces 23 and 22, and a multiplicity of spaced hook members 21projecting from at least the upper surface 23 of the strand 20. Thestrand 20 can have planar surfaces or surface features as could bedesired for tear resistance or reinforcement. The strands 20 areseparated from each other by cuts and elongation of ribs 8. As is bestseen in FIGS. 6 a and 6 b, the hook members 21 each comprise a stemportion 15 attached at one end to a strand 20 and preferably havingtapered sections 16 that widen toward the strand 20 to increase the hookanchorage and breaking strengths at their junctures with a strand 20,and a head portion 17 at the end of the stem portion 15 opposite strand20. The sides 34 of the head portion 17 can be flush with the sides 35of the stem portion 15 on two opposite sides. The head portion 17 hashook engaging parts or arms 36, 37 projecting past the stem portion 15on one or both sides 38. The hook member shown in FIGS. 6 a and 6 b canhave a rounded surface 18 opposite the stem portion 15. The head portion17 shown also has transverse cylindrically concave surface portions 19at the junctures between the stem portion 15 and the surfaces of thehead portion 17 projecting over strand 20.

With reference to FIGS. 6 a and 6 b, there is shown a singlerepresentative one of the small hook members 21 on which its dimensionsare represented by reference numerals between dimensional arrows. Theheight dimension is 30. The stem and head portions 15 and 17 have athickness dimension 25, which as shown is the same, and the headportions 17 have a width dimension 27 and an arm droop 24. The stemportion has a width dimension 26 at its base before flaring 16 to thestrand 20. The thickness as shown is for a rectilinear shaped hook, withother shapes the thickness can be measured as the shortest distancebetween two opposing sides 34 or 35. Likewise, the width dimension canbe measured as the shortest distance between two opposing sides.

FIGS. 7 and 8 illustrate two of many alternate shapes that could be usedfor the hook members in alternate embodiments of the hook members thatcan be formed in accordance with the invention method.

The hook member 45 illustrated in FIG. 7 differs from the hook member 21of FIG. 5 in that its head portion 46 projects farther on opposite sidesfrom its stem portion 47 and is generally uniformly thick so that it canmore easily bend to engage with or disengage from loops on a loopfastener portion.

The hook member 60 illustrated in FIG. 8 differs from the hook member 21of FIG. 5 in that its head portion 61 projects from only one side of itsstem portion 62 and will thus cause significantly greater peel forceswhen peeled away from the direction the head portion 61 projects thanwhen it is peeled toward the direction the head portion 61 projects.

With all of these hook shapes the hook shape and dimensions can bealtered following formation by heat treatment of at least the hookelements. Heat treating in particular will tend to shrink the hook widthin the direction that the ribs where extruded, by relaxing any molecularorientation in the hooks as a result of the extrusion of the ribs. Inthis case the width of the hooks can be less than that of the strandsfrom which the hooks project.

Suitable polymeric materials from which the netting of the invention canbe made include thermoplastic resins comprising polyolefins, e.g.polypropylene and polyethylene, polyvinyl chloride, polystyrene, nylons,polyester such as polyethylene terephthalate and the like and copolymersand blends thereof. Preferably the resin is a polypropylene,polyethylene, polypropylene-polyethylene copolymer or blends thereof.

An extruded hook netting is shown in FIG. 10, which results in hookfastening elements on both faces of the netting. Generally, with a hooknetting as shown in FIG. 10, the precursor film has elongate spaced ribsthat project from both surfaces of the base layer where each set of ribshas a cross-sectional shape of the hook portions or members to beformed. The ribs on one face are partially transversely slit at spacedlocations along their lengths. The entire ribs and the base layer on theother face are fully cut as per, e.g., the FIG. 5 embodiment. When thepartially cut ribs are longitudinally elongated or stretched, as per theFIG. 5 embodiment, they form hook elements 72 and oriented ribs 78.Simultaneously with longitudinal stretching, the cut base layer andother set of ribs form transverse strands 70 and hook elements 71, onthe strands 70.

FIG. 9 shows an embodiment 80 where the secondary ribs 81 are not in theform of hooks in their cross sectional profile. This will result instems being formed on the secondary strands 89 that could besubsequently formed into hook elements such as by the method describedin U.S. Pat. Nos. 6,368,097 and 6,132,660, the substance of which isincorporated herein by reference.

The invention extruded hook netting, such as shown in FIGS. 5 and 10, ishighly breathable and dimensionally stable, in at least the direction oforiented strands 8 or 78. The longitudinal dimensional stability meansthat the netting will have essentially the same dimensions whenuntensioned and when placed under moderate tension. Further, theinvention would also be dimensionally stable in the direction of thetransverse strands cut from the base layer particularly if thetransverse strands are at substantially right angles to the orientedstrands. These transverse strands can also be oriented to increase theirmechanical strength and reduce their basis weight while increasing theirflexibility and dimensional stability. In a particularly preferredapplication, the material is self-mating with itself and as such is anextremely low cost and highly functional as a bundling material such asa bundling strap, a vegetable wrap or like applications wherebreathability and self engageability are important. The extruded hooknetting in particular could find use in disposable garment applicationssuch as headbands, diapers, incontinent briefs, feminine hygienearticles and the like where it is desirable to have an engaging materialthat would conform to a user and provide breathability. In these andother applications, the hook netting could also be laminated to otherstructures by conventional techniques such as adhesive lamination,thermal or pressure welding, such as fibrous webs (e.g., nonwovenfibrous knitted or stitch bonded fibrous materials), films orthree-dimensional structures.

Test Methods

135 Degree Peel Test

The 135 degree peel test was used to measure the amount of force thatwas required to peel a sample of the mechanical fastener hook materialfrom a sample of loop fastener material. A 5.1 cm×12.7 cm piece of aloop test material was securely placed on a 5.1 cm×12.7 cm steel panelby using a double-coated adhesive tape. The loop material was placedonto the panel with the cross direction of the loop material parallel tothe long dimension of the panel. A 1.9 cm×2.5 cm strip of the mechanicalfastener to be tested was cut with the long dimension being in themachine direction of the web. A 2.5 cm wide paper leader was attached tothe smooth side of one end of the hook strip. The hook strip was thencentrally placed on the loop so that there was a 1.9 cm×2.5 cm contactarea between the strip and the loop material and the leading edge of thestrip was along the length of the panel. The strip and loop materiallaminate was then rolled by hand, twice in each direction, using a 1000gram roller at a rate of approximately 30.5 cm per minute. The samplewas then placed in a 135 degree peel jig. The jig was placed into thebottom jaw of an Instron™ Model 1122 tensile tester. The loose end ofthe paper leader was placed in the upperjaw of the tensile tester. Acrosshead speed of 30.5 cm per minute and a chart recorder set at achart speed of 50.8 cm per minute was used to record the peel force asthe hook strip was peeled from the loop material at a constant angle of135 degrees. An average of the four highest peaks was recorded in grams.The force required to remove the mechanical fastener strip from the loopmaterial was reported in grams/2.54 cm-width. A minimum of 10 tests wererun and averaged for each hook and loop combination.

Two different loop materials were used to measure the performance of themechanical fastener hook material. Loop material ‘A’ is a nonwoven loopmade similar to that described in U.S. Pat. No. 5,616,394 Example 1,available from the 3M Company as KN-1971. Loop material ‘B’ is a knittedloop made similar to that described in U.S. Pat. No. 5,605,729, Example1 available from the 3M Company as XML-01-160. The loop test materialswere obtained from a supply roll of the material after unwinding anddiscarding several revolutions to expose “fresh” material. The loop testmaterial thus obtained was in a relatively compressed state and was usedimmediately in the peel test before any significant relofting of theloops could occur.

Dynamic Shear

The dynamic shear test was used to measure the amount of force requiredto shear the sample of mechanical fastener hook material from a sampleof loop fastener material. A 2.5 cm×7.5 cm loop sample was cut with theshort dimension being the machine direction of the hook. This loopsample was then reinforced with 3M strapping tape on the backside of theloop. A 1.25 cm×2.5 cm hook sample was also prepared. The long dimensionis the machine direction of the hook. This sample was laminated to theend of a tab of 3M strapping tape 2.5 cm wide×7.5 cm long. The strappingtape was doubled over on itself on the end without hook to cover theadhesive. The hook was then placed centrally on the loop with long tabdirections parallel to each other such that the loop tab extended paston the first end and the hook tab extended past on the second end. Thehook was rolled down by hand with a 5 kg rolldown 5 replicates up andback. The assembled tabs were placed into the jaws of an Instron Model1122 tensile tester. The hook tab placed in the top jaw, the loop tabplaced in the bottom jaw. A crosshead speed of 30.5 cm per minute and achart recorder set at a chart speed of 50.8 cm per minute was used torecord the shear force as the hook strip was sheared from the loopmaterial at a constant angle of 180 degrees. The maximum load wasrecorded in grams. The force required to shear the mechanical fastenerstrip from the loop material was reported in grams/2.54 cm-width. Aminimum of 10 tests were run and averaged for each hook and loopcombination.

Hook Dimensions

The dimensions of the hook materials were measured using a Leicamicroscope equipped with a zoom lens at a magnification of approximately25×. The samples were placed on a x-y moveable stage and measured viastage movement to the nearest micron. A minimum of 3 replicates wereused and averaged for each dimension. In reference to the Example hooks,as depicted generally in FIGS. 6 a and 6 b, hook width is indicated bydistance 27, hook height is indicated by distance 30, arm droop isindicated by distance 24, and hook thickness is indicated by distance25. The dimensions of the hook materials of the invention are shown inTable 1 below.

EXAMPLE 1

A mesh hook netting was made using apparatus similar to that shown inFIG. 1. A polypropylene/polyethylene impact copolymer (SRC7-644, 1.5MFI, Dow Chemical) was extruded with a 6.35 cm single screw extruder(24:1 L/D) using a barrel temperature profile of 175° C.-230° C.-230° C.and a die temperature of approximately 230° C. The extrudate wasextruded vertically downward through a die having an opening cut byelectron discharge machining to produce an extruded profiled web similarto that shown in FIG. 6 a and referred to below as precursor web. Thecrossweb spacing of the upper ribs was 7.3 ribs per cm. After beingshaped by the die, the extrudate is quenched in a water tank at a speedof 6.1 meter/min with the water being maintained at approximately 10° C.The web was then advanced through a cutting station where the upper ribsand the base layer (but not the lower ribs) were transversely cut at anangle of 23 degrees measured from the transverse direction of the web.The spacing of the cuts was 305 microns. After cutting the upper ribsand the base layer, the reticulated web was longitudinally stretched ata stretch ratio of approximately 3 to 1 between a first pair of niprolls and a second pair of nip rolls to further separate the individualhook elements to approximately 8.5 hooks/cm to produce a hook nettingsimilar to that shown in FIG. 5. The thickness of the base layer was 219microns. The upper roll of the first pair of nip rolls was heated to143° C. to soften the web prior to stretching. The second pair of niprolls were cooled to approximately 10° C.

EXAMPLE 2

The netting of Example 1 was subjected to a non-contact heat treatmenton the hook side of the netting by passing the netting at 7.3 meters/minthrough a gap defined by a heated support roll and a curvilinearperforated metal plate. The perforations were approximately 0.6 cm indiameter and spaced approximately 3.0 cm from each other. The nettingwas treated over a radial distance of the 46 cm. Hot air at atemperature of approximately 185° C., provided by a 15 kW electricheater, was blown through the perforations in the metal plate onto thehook side of the netting at a velocity of approximately 3350 meter/min.The hooks were approximately 2.5 cm from the perforated plate. Thesmooth base film side of the web was supported on the heated roll atapproximately 149° C. After heat treatment the web was cooled by passingthe web over a chill roll maintained at 52° C.

EXAMPLE 3

The precursor web of Example 1 was biaxially stretched in a Karo IVpantograph film stretcher (Bruchner Gmbh) using a chamber temperature of150° C. The web was preheated for one minute at 150° C. and thensimultaneously stretched 3× in the machine direction (MD) and 2.8× inthe cross direction (CD) at an interval of 0.67 seconds MD and a 60second interval CD.

EXAMPLE 4

A web was made as in Example 1 except the thickness of the base layerwas 150 microns.

TABLE 1 Example Precursor Web 1 2 3 4 Hook Width (μ) 550 498 524 567 517Hook Height (μ) 564 566 556 514 562 Hook Droop (μ) 249 229 292 192 229Hook Thickness (μ) 307 327 267 302 306 Base Thickness (μ) 214 219 199 98150 Rib Width (μ) 512 285 266 382 279 Rib Height (μ) 545 257 283 235 363Hook Spacing (CD, /cm) 7.3 9.0 8.9 3.6 8.3 Hook Spacing (MD, /cm) 25.58.5 7.8 6.8 7.7

TABLE 2 Peel Strength Peel Strength Shear Strength Shear Strength LoopMaterial ‘A’ Loop Material ‘B’ Loop Material ‘A’ Loop Material ‘B’Example (gms/2.54 cm) (gms/2.54 cm) (gms/2.54 cm) (gms/2.54 cm) 1 358217 3428 3550 4 346 312 1524 2692

1. A polymer netting comprising a plurality of oriented thermoplasticstrands extending in a first direction, the first set of orientedstrands having a first face and a second face and two side faces, asecond set of strands integrally formed with the first set of orientedstrands and attached only to said first face of said oriented strands,wherein said first set of oriented strands occupy a first planarcross-sectional area in the thickness direction of the netting and saidsecond set of strands occupy a second planar cross-sectional area in thethickness direction of the netting and said first and second planarcross-sectional areas are substantially mutually exclusive and abuttingand said second set of strands has substantially parallel side facessuch that the strand width of the second set of strands at crossoverpoints of the two sets of strands is substantially the same as thestrand width of the second set of strands between the crossover points,and wherein said second set of strands have surface structures on saidfirst faces of the strands.
 2. The polymer netting of claim 1 whereinsaid second set of strands are mutually parallel and have a first faceand a second face and are substantially coextensive.
 3. The polymernetting of claims 2 wherein said second set of strands second faces areattached to said first set of oriented strands at their crossoverpoints.
 4. The polymer netting of claim 1 wherein said second set ofstrands have a substantially rectilinear cross-section.
 5. The polymernetting of claim 4 wherein adjacent strands of said second set ofstrands have a substantially identical cross-sectional shape in saidfirst direction.
 6. The polymer netting of claim 1 wherein said secondset of strands are linear.
 7. The polymer netting of claim 1 whereinsaid surface structures are stems extending upward.
 8. The polymernetting of claim 7 wherein said stem structures have hook elementsprojecting in at least one direction.
 9. The polymer netting of claim 8wherein said hook elements extend in the direction of the second set ofstrands.
 10. The polymer netting of claim 8 wherein said hook elementsextend in two or more directions and form a mushroom.
 11. The polymernetting of claim 1 wherein said first set of strands have surfacestructures on said second face of said strands.
 12. The polymer nettingof claim 11 wherein said surface structures are stems extending upward.13. The polymer netting of claim 12 wherein said stem structures havehook elements projecting in at least one direction.
 14. The polymernetting of claim 13 wherein said hook elements extend in a directionperpendicular to said first direction.
 15. The polymer netting of claim1 wherein said polymer is a thermoplastic polymer.